Rana Mukherji ¹, Vishal Mathur ², Arvind Samariya ³, Manishita Mukherji ⁴

Affiliations
1 The ICFAI University, Jaipur – 302031, Rajasthan, IN
2 The ICFAI University, Jaipur – 302031, Rajasthan
3 S. S. Jain Subodh P.G. College, Jaipur – 302004, Rajasthan, IN
4 Amity University Rajasthan, Jaipur – 303007, Rajasthan, IN

Abstract

Objective: Multivariate statistical analysis viz. Cluster Analysis (CA) was performed to validate the experimental findings. Methods/Statistical Analysis: The (In_0.955CO_0.045)₂O₃ samples were concocted by the typical solid state reaction route. The resulting materials were pelletized and sintered in hydrogen atmosphere. Subsequently, hydrogenated pallets were dehydrogenated by further heating for 7h in air. The samples were thoroughly characterized using X-ray diffraction. FULLPROF Program is used to refine the crystalline structures. Magnetic hysteresis loops were evaluated using Vibrating Sample Magnetometer (VSM) at room temperature. Hierarchical CA was accomplished on the normalized data set (samples) by means of the Ward's method, using Euclidean distances as a measure of similarity. Findings: The X-Ray Diffraction (XRD) study confirmed the formation of cubic bixbyite structure for In₂O₃, In_0.955CO_0.045)₂O₃ and In_0.955CO_0.045)₂O₃:H samples. The magnetic study at Room Temperature (RT) confirms that pure In₂O₃

Keywords

Cluster Analysis, Hydrogen, In₂O₃, Magnetic Properties, Post-Annealing.

Full Text