Photocurrent Enhancement of Cu/p-CuSCN/n-Cu2O Quantum Dot (QD) Novel Solid State Photovoltaic Cell with Coconut Shell Activated Carbon (CAC) as the Upper Electrode


Affiliations
1 Nano-Technology Research Laboratory, Department of Electronics, Wayamba University of Sri Lanka, Kuliyapitiya, Sri Lanka
2 Department of Biotechnology, Wayamba University of Sri Lanka, Makandura, Sri Lanka
     

   Subscribe/Renew Journal


p-CuSCN was sensitized by n-Cu2O quantum dots (QDs) to fabricate a new solid state photovoltaic cell. QDs of n-Cu2O were deposited by boiling Cu/p-CuSCN photoelectrodes in a 1M CuSO4 solution to form Cu2O QDs on p-CuSCN. Boiling periods controlled the n-Cu2O quantum dot size. Activated coconut shell charcoal (CAC) was introduced on top of the Cu2O as the upper electrode and finally ITO glass was placed on CAC to fabricate the device.

Keywords

N-Cu2O, P-CuSCN, Quantum Dots.
User
Subscription Login to verify subscription
Notifications
Font Size

Abstract Views: 196

PDF Views: 2




  • Photocurrent Enhancement of Cu/p-CuSCN/n-Cu2O Quantum Dot (QD) Novel Solid State Photovoltaic Cell with Coconut Shell Activated Carbon (CAC) as the Upper Electrode

Abstract Views: 196  |  PDF Views: 2

Authors

P. G. D. C. K. Karunarathna
Nano-Technology Research Laboratory, Department of Electronics, Wayamba University of Sri Lanka, Kuliyapitiya, Sri Lanka
C. A. N. Fernando
Nano-Technology Research Laboratory, Department of Electronics, Wayamba University of Sri Lanka, Kuliyapitiya, Sri Lanka
S. N. T. De Silva
Department of Biotechnology, Wayamba University of Sri Lanka, Makandura, Sri Lanka

Abstract


p-CuSCN was sensitized by n-Cu2O quantum dots (QDs) to fabricate a new solid state photovoltaic cell. QDs of n-Cu2O were deposited by boiling Cu/p-CuSCN photoelectrodes in a 1M CuSO4 solution to form Cu2O QDs on p-CuSCN. Boiling periods controlled the n-Cu2O quantum dot size. Activated coconut shell charcoal (CAC) was introduced on top of the Cu2O as the upper electrode and finally ITO glass was placed on CAC to fabricate the device.