Journal of Surface Science and Technology

M. A. Rahman ¹, M. A. K. Azad ¹, S. Ahsan ¹, S. Islam ¹, M. A. Motin ¹, M. Asadullah ¹

Affiliations
1 Department of Applied Chemistry and Chemical Technology, University of Rajshahi, Rajshahi 6205, BD

Abstract

Silica-Alumina catalysts having three different Si/Al ratios were prepared. Surface acidity of these catalyst samples was measured by the base exchange method using aqueous ammonium acetate, CH₃COONH₄ solution and the results were compared with those measured by the base exchange method using KOH and NH₄OH as adsorbates from aqueous solution. The amount of K⁴ and NH₄⁺ adsorbed was determined titrimetrically and spectrophotometrically, respectively for measuring the concentration of K⁺ and NH₄⁺ in the solution before and after adsorption. It was found that the surface acidity was more pronounced when ammonium acetate solution was used as an adsorbate. With the use of NH₄OH and KOH as bases considerable dealumination takes place with a consequent decrease of surface acidity of the catalyst samples. In all cases, the surface acidity increased with decrease of sample size. It is seen that surface acidity measured with NH₄OH becomes closer to that measured with KOH at the same(?) Si/Al ratio, but contrary to this, surface acidity measured with NH₄OH becomes closer to that measured with CH₃COONH₄ at high Si/Al ratio. This phenomenon is attributed to dealumination of silica-alumina catalyst samples by the strong base.

Keywords

Surface Acidity, Silica-Alumina Catalysts, Bronsted Acidity, Base Exchange.

Full Text