Effects of magnesium silicate and alumina dispersed in engine lubricant on friction, wear, and tribosurface characteristics are studied under boundary and mixed lubrication conditions.Magnesiumsilicate and alumina, henceforth called as friction reducing compounds (FRC), were dispersed in engine lubricant in very low concentration of 0.01% weight/volume. Four-ball wear test rig was used to assess friction coefficient and wear scar diameter of balls lubricated with and without FRC based engine lubricant. Scanning electron microscopy (SEM) equipped with Energy Dispersive X-ray (EDX) was used to analyse the tribosurface properties and elemental distributions on worn surfaces of the balls. Test results revealed that FRC based engine lubricant increases friction coefficient but marginally reduces wear scar diameter of new balls, whereas, test on the worn-out balls running on FRC based engine lubricants shows 46% reduction in friction coefficient compared to the new balls running on engine lubricants without FRC. Investigations on tribosurfaces with respect to morphology and elemental distribution showed the presence of Si and O elements in micropores of the worn surfaces of the balls, indicating role of FRC in friction coefficient reduction and antiwear properties. These FRC based engine lubricants may be used in the in-use engines.
User
Notifications
Font Size